Lithography using high selectivity spacers for pitch reduction

ABSTRACT

A method embodiment for patterning a semiconductor device includes patterning a dummy layer over a hard mask to form one or more dummy lines. A sidewall aligned spacer is conformably formed over the one or more dummy lines and the hard mask. A first reverse material layer is formed over the sidewall aligned spacer. A first photoresist is formed and patterned over the first reverse material layer. The first reverse material layer using the first photoresist as a mask, wherein the sidewall aligned spacer is not etched. The one or more dummy lines are removed, and the hard mask is patterned using the sidewall aligned spacer and the first reverse material layer as a mask. A material used for forming the sidewall aligned spacer has a higher selectivity than a material used for forming the first reverse material layer.

PRIORITY CLAIM AND CROSS REFERENCE

This application is a continuation of U.S. patent application Ser. No. 14/096,864, filed Dec. 4, 2013, entitled “Lithography Using High Selectivity Spacers for Pitch Reduction,” which application is hereby incorporated herein by reference in its entirety.

BACKGROUND

With the increasing down-scaling of semiconductor devices, various processing techniques, such as, photolithography are adapted to allow for the manufacture of devices with increasingly smaller dimensions. However, as semiconductor processes require smaller process windows, the manufacture of these devices have approached and even surpassed the theoretical limits of photolithography equipment. As semiconductor devices continue to shrink, the spacing desired between elements (i.e., the pitch) of a device is less than the pitch that can be manufactured using traditional optical masks and photolithography equipment.

One approach used to achieve the higher resolutions to manufacture, for example, 40 nm or smaller devices, is to use multiple pattern lithography. For example, a “half pitch” (half of the minimum photolithographic pitch achievable in a traditional photolithography system) can be achieved by forming dummy lines (e.g., at a minimum available pitch), forming sidewall aligned spacers on the dummy lines, removing the dummy lines while leaving the spacers, and then using the spacers as patterning masks to transfer the desired pattern to underlying layers. In this manner, line spacing at approximately half the minimum pitch can be achieved.

The disposition of additional materials (e.g., reverse material layers) for additional lithography patterning and cutting may be performed on the spacers prior to the removal of the dummy lines. This additional patterning/cutting allows for greater variation and/or more complex patterns to be formed in semiconductors for back end of line (BEOL) processes with small pitches. However, traditional techniques for additional patterning/cutting rely on multiple planarization steps, which increase the achievable process window and increase manufacturing cost.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the present embodiments, and the advantages thereof, reference is now made to the following descriptions taken in conjunction with the accompanying drawings, in which:

FIGS. 1 through 17B illustrate various cross-sectional and elevation views of intermediate stages of patterning a hard mask in accordance with various embodiments.

DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS

The making and using of the present embodiments are discussed in detail below. It should be appreciated, however, that the present disclosure provides many applicable inventive concepts that can be embodied in a wide variety of specific contexts. The specific embodiments discussed are merely illustrative of specific ways to make and use the disclosed subject matter, and do not limit the scope of the different embodiments.

Various embodiments provide a method for patterning a semiconductor device layer by transferring a pattern to a hard mask disposed over the semiconductor device layer. Dummy lines are formed over the hard mask. The dummy lines may be spaced apart at a minimum pitch that a photolithographic system can achieve. A sidewall aligned spacer is conformably deposited over the dummy lines. The sidewall aligned spacer comprises a high selectivity material such as titanium nitride or titanium oxide.

In order to form additional patterns (e.g., of a different width than the spacer and/or more complex patterns that may include patterns in a different direction than the spacer/dummy lines), reverse material layers are formed and patterned over the spacer. For example, two reverse material layers may be formed and patterned over the spacer for complex patterns. The first reverse material layer may be patterned using a selective etching process using a patterned photoresist formed over the reverse material layer as a mask. Because the spacer is formed of a high selectivity material, the etching of the first reverse material layer does not etch the spacer. The patterning of the first reverse material layer may be done to transfer patterned lines of different widths than the spacer to the hard mask. The patterning of a second reverse material layer may be done to transfer a more complex pattern, for example, running in a direction perpendicular to the spacer/dummy lines to the hard mask. Alternatively, for less complex patterns, the second reverse material layer may be excluded.

An etch back may then be performed to expose the dummy lines, which are then removed. The hard mask is then patterned using the spacer and reverse material layers as a mask. Because the spacer was formed along both sidewalls of the dummy lines, the spacer may be patterned at about half the pitch of the dummy lines. Furthermore, due to the high selectivity of the spacer, the reverse material layers may be etched directly compared to traditional methods, which rely on multiple planarization steps. Thus, the number of process steps needed to pattern the reverse material layers are lowered, reducing manufacturing cost and improving process reliability.

FIG. 1 illustrates a cross-sectional view of a portion of a semiconductor device 100 in accordance with various embodiments. Semiconductor device 100 includes a layer 102 that requires patterning. Layer 102 may be a metallic layer (e.g., copper, aluminum, and the like), a dielectric layer, a polymer layer, a substrate (e.g., silicon), or any other layer of a semiconductor device that may be patterned using photolithography and etching techniques. A hard mask 104 is disposed over layer 102. Hard mask 104 may be formed of any suitable material such as silicon oxynitride (SiON), silicon nitride (Si₃N₄), titanium nitride (TiN) or the like. Hard mask 104 may be formed by chemical vapor deposition (CVD), low pressure CVD, plasma enhanced CVD, or the like. In subsequent process steps, a pattern is transferred onto hard mask 104 using various photolithography and etching techniques. Hard mask 104 may then be used as a patterning mask for etching underlying layer 102.

A dummy layer 106 is disposed over hard mask 104. Dummy layer 106 may be etched to form dummy line patterns for the formation of sidewall aligned spacers in multiple pattern lithography. Dummy layer 106 may be a polymer, an ashable hard mask (e.g., amorphous carbon film or amorphous silicon film), polysilicon, or any other material that may be patterned and selectively removed.

A bi-layer photoresist 114 may be formed over dielectric hard mask layer 108, which may comprise a hard mask material such as a nitride (e.g., SiON). Bi-layer photoresist includes a top photoresist layer 112, and a bottom layer 110, which may include anti-reflective materials (e.g., a bottom anti-reflective coating (BARC) layer) to aid the exposure and focus of the top photoresist layer 112's processing.

FIG. 2 illustrates the patterning of top photoresist layer 112 using any suitable photolithography technique. For example, a photomask (not shown) may be disposed over top photoresist layer 112, which may then be exposed to radiation such as ultraviolet light or an exciser laser. Exposure of top photoresist layer 112 may be performed using an immersion lithography system (e.g., a 193 nm immersion lithography system) to increase resolution and decrease the minimum achievable pitch. A bake or cure operation may be performed to harden top photoresist layer 112, and a developer may be used to remove either the exposed or unexposed portions of the layer 112 depending on whether a positive or negative resist is used. Thus, a pattern such as the pattern illustrated in FIG. 2 is formed in top photoresist layer 112. The patterned portions of top photoresist layer 112 may be spaced apart from each other at a pitch P. Pitch P may be a minimum pitch (i.e., the smallest pitch the photolithographic system can achieve) and may be, for example, about 80 nm. The pattern of photoresist layer 112 in FIG. 2 is for illustrative sake only, and other patterns may be formed depending on the design of semiconductor device 100.

FIG. 3 illustrates the transferring of the pattern of top photoresist layer 112 to bottom layer 110 and a dielectric hard mask layer 108, respectively. Dielectric hard mask layer 108 may be formed of any suitable material, such as, a nitride (e.g., SiON). The pattern transfer may be done, for example, using a selective etchant process. Subsequently, top and bottom layers 112 and 110 may be etched using, e.g., a trimming process such as anisotropic plasma etch process. Portions of dielectric hard mask layer 108 may also be removed as part of the trimming process to achieve a more stable, aspect-ratio for subsequent etching steps. Referring now to FIG. 4, dummy layer 106 may be etched using bi-layer photoresist 114 and dielectric hard mask layer 108 as a patterning mask, forming dummy lines 106A, 106B, and 106C (sometimes referred to as mandrels 106A-106C).

In FIG. 5A, bi-layer photoresist 114 and dielectric hard mask layer 108 may then be removed by applying, for example, an ashing process and a wet clean process to clean the remainder of dielectric hard mask layer 108 from the patterned dummy layer 106 lines. The use of bi-layer photoresist 114 and the dielectric hard mask layer 108 to pattern dummy layer 106 allows for dummy lines 106A-106C to have evenly spaced, substantially rectangular profiles for the stable formation of a sidewall aligned spacer in a subsequent process step. Other techniques for patterning dummy layer 106 may also be used.

FIG. 5B illustrates a top down view of the semiconductor device 100 illustrated in FIG. 5A. As shown in FIG. 5B, a plurality of dummy lines 106A, 106B, and 106C run in parallel corresponding to a pattern defined by bi-layer photoresist 114. Patterned dummy lines 106A-106C may be spaced apart from each other by pitch P (e.g., 80 nm). Although three dummy lines are illustrated in FIGS. 5A and 5B, various embodiments may include a different number of dummy lines depending on the patterning of bi-layer photoresist 114 and the design of semiconductor device 100.

FIG. 6A illustrates the formation of a sidewall aligned spacer 116 over dummy lines 106A-106C and hard mask 104. Spacer 116 may be conformably formed over dummy lines 106A-106C using any suitable method such as atomic layer deposition (ALD), CVD, low pressure CVD, or the like. The material used for spacer 116 may have a high selectivity that is greater than materials deposited for subsequent patterning steps (e.g., illustrated in FIGS. 7-16). That is, the material of spacer 116 may have a high selectivity (e.g., greater than 5 or 6) so that subsequent etching steps may be performed on materials over spacer 116 without significantly attacking the material of spacer 116. Thus, spacer 116 may also be referred to as a high selectivity spacer. In various embodiments, spacer 116 may be formed of titanium nitride (TiN), titanium oxide (TiO), or the like. Furthermore, the thickness of spacer 116 may be selected to determine the thickness of features eventually formed in semiconductor device layer 102.

FIG. 6B illustrates a top-down view of the semiconductor device 100 shown in FIG. 6A. Spacer 116 conformably covers a top surface of semiconductor device 100. Dummy lines 106A-106C are illustrated in ghost in FIG. 6B for reference. Raised edges of spacer 116 around dummy lines 106A-106C are indicated by dashed outlines 116′. As shown in FIG. 6B, spacer 116 may be formed around all four sides of dummy lines 106A-106B uniformly.

Referring now to FIG. 7, a reverse material layer 118 may be formed over spacer 116. In various embodiments, reverse material layer 118 may be spun on glass (SOG) or any other suitable material.

In FIG. 8A, top portions of reverse material layer 118 may be etched back to expose top surfaces of spacer 116, using, for example an anisotropic etching technique. Notably, a top surface reverse material layer 118 may be lower than, and not level with, a top surface of spacer 116. FIG. 8B illustrates a top down view of semiconductor device 100 shown in FIG. 8A. As illustrated in FIG. 8B, the etch back of reverse material layer 118 exposes the portions of spacer 116 surrounding dummy lines 106A-106C (shown in ghost for reference).

FIG. 9 illustrates the formation of a tri-layer photoresist 126 over spacer 116 and reverse material layer 118. Tri-layer photoresist 126 includes a relatively thin top photoresist layer 124, a middle layer 122, and a bottom layer 120. As the limits of photolithography processes are reached by advanced semiconductor manufacturing processes, the need for thinner top photoresist layers has arisen to achieve smaller process windows. However, thin top photoresist layers may not be sufficiently robust to support the etching of target layers. A tri-layer photoresist provides a relatively thin top photoresist layer 124. Tri-layer photoresist 126 further includes a middle layer 122, which may include silicon-containing photoresist materials to increase the selectivity of bottom layer 120. Tri-layer photoresist 126 further includes a bottom layer 120, which may comprise a photoresist spin-on material. Thus, tri-layer photoresist 126 allows for the robust patterning of underlying layers (e.g., dummy layer 118) while still providing a relatively thin top photoresist layer 124.

FIGS. 10A and 10B illustrate the patterning of top photoresist layer 124. FIG. 10A shows a cross-sectional view, and FIG. 10B shows a top-down view. The cross-sectional view illustrated in FIG. 10A may be taken across the line 10A/10A of FIG. 10B. The patterning of top photoresist layer 124 may be achieved, for example, by using an immersion photolithography system (e.g., a 193i system) to expose portions of top photoresist layer 124 and developing the exposed/unexposed portions depending on whether a positive/negative photoresist is used. Top photoresist layer 124 may be patterned to not cover certain areas of reverse material layer 118, including portions between dummy lines 106A and 106C. Additional portions of reverse material layer 118 may also be uncovered, which may be used to eventually transfer patterns of varying dimensions to hard mask 104 in subsequent process steps.

FIGS. 11A and 11B illustrate the patterning of reverse material layer 118 using tri-layer photoresist 126. FIG. 11A shows a cross-sectional view of semiconductor device 100 taken across the line 11A/11A of the top-down view illustrated in FIG. 11B. Reverse material layer 118 may be selectively patterned, for example, by selectively etching reverse material layer 118 using tri-layer photoresist 126 as a patterning mask. The chemical etchant used may be selected to etch only reverse material layer 118 without significantly etching spacer 116. For example, tetrafluoromethane (CF₄), trifluoromethane (CHF₃), difluoromethane (CH₂F₂), octafluorocyclobutane (C₄F₈), or the like may be used to selectively etch the material of reverse material layer 118 (e.g., SOG) because C_(x)F_(y) may not significantly attack the high selectivity material of spacer 116 (e.g., TiN or TiO). Other suitable chemical etchants may also be used. Thus, reverse material layer 118 may be patterned directly without the use of multiple planarization processes.

The remaining patterned portions of reverse material layer 118 may be referred to as a line B pattern. This line B pattern may be used to transfer features of varying dimensions (e.g., widths) to hard mask 104 and semiconductor device layer 102 in subsequent process steps. Portions of the line B pattern (e.g., 118A) pattern may be used to increase the width of spacer 116 while other portions of the line B pattern (e.g., 118B) may be used to create new pattern features of a different width than spacer 116. The patterns shown in FIGS. 11A and 11B are for illustrative purposes only and different patterns may be formed depending on the design of semiconductor device 100.

FIGS. 12A and 12B illustrate the formation of a tri-layer photoresist 134 and the patterning of a top photoresist layer 132. Tri-layer photoresist 134 may be substantially similar to tri-layer photoresist 126 and includes a relatively thin top photoresist layer 132, a middle layer 130, and a bottom layer 128. FIG. 12A shows a cross-sectional view, and FIG. 12B shows a top-down view. The cross-sectional view illustrated in FIG. 12A may be taken across the line 12A/12A of FIG. 12B. The patterning of top photoresist layer 132 may be achieved, for example, using an immersion photolithography system (e.g., a 193i system) to expose portions of top photoresist layer 132 and developing the exposed/unexposed portions depending on whether a positive/negative photoresist is used.

Top photoresist layer 132 may be patterned create openings over semiconductor device 100. These openings, which may be referred to as cut B patterns, may be used to eventually transfer more complex patterns, for example, in a perpendicular direction to patterns of spacer 116 and the line B pattern to hard mask 104 or to form different pattern shapes in subsequent process steps. Because the line B pattern is defined by a separate lithography step (e.g., as illustrated by FIGS. 11A and 11B), the line B pattern is not limited by the pattern and width of spacers 116. Thus, various embodiments provide additional flexibility in forming the line B pattern through lithography and optional cut B patterning, for example, to provide for patterns of varying widths and shapes.

FIG. 13 illustrates the etching of bottom layer 128 using top photoresist layer 132 and middle layer 130 as a mask. The chemical etchant used on bottom layer 128 may be selected to etch only bottom layer 128, without significantly etching spacer 116. For example, tetrafluoromethane (CF₄) may be used to selectively etch the material of bottom layer 128 (e.g., SiON) as CF₄ may not significantly attack the higher selectivity material of spacer 116 (e.g., TiN or TiO). As bottom layer 128 is etched, top photoresist layer 132 may be simultaneously etched away. Thus, after the etching, top photoresist layer 132 may have been removed as a result of the etching.

FIG. 14 illustrates the coating of a reverse material layer 136 over semiconductor device 100, filling openings in bottom layer 128. Reverse material layer 136 may be substantially similar to reverse material layer 118. For example, reverse material layer 136 may be formed of spin on glass (SOG).

FIGS. 15A and 15B illustrate the removal of tri-layer photoresist 134 and the etch back of reverse material layer 136. FIG. 15A shows a cross-sectional view taken across the line 15A/15A of the top-down view illustrated in FIG. 15B. Tri-layer photoresist 134 may be removed, for example, using a combination of ashing and wet clean processes. The etch back of top portions of reverse material layer 136 exposes top surfaces of spacer 116, and may be performed, for example, using an anisotropic etching technique. Notably, a top surface reverse material layer 136 may be lower than, and not level with, a top surface of spacer 116. Furthermore, reverse material layer 136 forms more complex patterned portions, for example, that run in a direction perpendicular to and connecting portions of spacer 116 or to form varying shapes and widths. The exact pattern of reverse material layer 136 may vary in various embodiments depending on the design of semiconductor device 100. Alternatively, the formation and patterning of a second reverse material layer 136 (e.g., as illustrated in FIGS. 12A-15B) may be excluded in certain patterning processes, for example, involving less complex patterning.

FIGS. 16A and 16B illustrate etch back of spacer 116 and the removal of dummy lines 106. FIG. 16A shows a cross-sectional view taken across the line 16A/16A of the top-down view illustrated in FIG. 16B. Top portions of spacer 116 may be anisotropically etched to expose underlying dummy lines 106 and hard mask 104. The chemical etchant used to etch spacers 116 may be selected based on the higher selectivity spacer material. For example, top surfaces of spacer 116 may be etched using chlorine as an etchant. Dummy lines 106 may be removed using, for example, an oxygen-plasma ashing process. Subsequently, a wet clean process may also be applied to semiconductor device 100 to remove residual spacer and dummy line material. The remaining spacer 116 and reverse material layers 118 and 136 form a mask for transferring a pattern onto hard mask 104. Reverse material layer 118 creates a pattern of varying dimensions (e.g., width) compared to the uniform dimension of spacer 116. The formation and patterning of reverse material layer 136 may be used to create a more complex pattern, for example, in a direction perpendicular to spacer 116.

FIGS. 17A and 17B illustrate the patterning of hard mask 104. FIG. 17A shows a cross-sectional view taken across the line 17A/17A of the top-down view illustrated in FIG. 17B. Hard mask 104 is patterned using spacer 116, reverse material layer 118 (i.e., line B pattern), and reverse material layer 136 (i.e., cut B pattern) as a mask. Alternatively, in processes that do not include reverse material layer 136 (i.e., cut B patterns), spacer 116 and reverse material layer 118 may be used to pattern hard mask 104. Any suitable chemical, for example, CF₄ may be used to etch hard mask 104. In a subsequently process step (not shown), hard mask 104 may be used to transfer the illustrated pattern to semiconductor device layer 102, for example, through an etching process using hard mask 104 as a patterning mask.

The pattern of hard mask 104 may be spaced at about half the pitch of dummy lines 106. For example, if a minimum pitch (e.g., 80 nm) was used to pattern dummy lines 106, then the features of hard mask 104 may be spaced at about half the minimum pitch (e.g., 40 nm). Thus, though the use of the intermediary steps illustrated in FIGS. 1-17B, a hard mask may be patterned having a high resolution and small pitch while containing patterns having varying dimensions (e.g., width). The patterns may also optionally include more complex portions, for example, aligned in different directions. Furthermore, through the use of a highly selective material for the sidewall aligned spacer, reverse material layers may be patterned directly, eliminating the need for multiple planarization processes and lowering manufacturing cost.

In accordance with an embodiment, a method for patterning a semiconductor device includes patterning a dummy layer over a hard mask to form one or more dummy lines. A sidewall aligned spacer is conformably formed over the one or more dummy lines and the hard mask. A reverse material layer is formed over the sidewall aligned spacer. A photoresist is formed and patterned over the first reverse material layer. The reverse material layer is selectively etched using the first photoresist as a mask, wherein the sidewall aligned spacer is not etched. The one or more dummy lines are removed, and the hard mask is patterned using the sidewall aligned spacer and the first reverse material layer as a mask. A material used for forming the sidewall aligned spacer has a higher selectivity than a material used for forming the first reverse material layer.

In accordance with another embodiment, a method for patterning a semiconductor device includes forming dummy lines over a hard mask and conformably forming a high selectivity spacer over the dummy lines. A first reverse material layer is formed over the high selectivity spacer. The first reverse material layer is etched back to expose a top surface of the high selectivity spacer. A photoresist is formed and patterned over the first reverse material layer. The first reverse material layer is selectively etched using the photoresist as a mask. A second reverse material layer is formed over portions of the high selectivity spacer. The dummy lines are removed, and the hard mask is patterned using the high selectivity spacer, the first reverse material layer, and the second reverse material layer as a mask

In accordance with yet another embodiment, a method for patterning a semiconductor device includes patterning a dummy layer over a hard mask layer in the semiconductor device to form one or more dummy lines and conformably forming a high selectivity spacer over the one or more dummy lines and the hard mask. A first reverse material layer is formed over the high selectivity spacer and etched back to a level below a top surface of the high selectivity spacer. A photoresist is patterned over the first reverse material layer. The first reverse material layer is selectively patterned using the photoresist as a mask, wherein the high selectivity spacer is not patterned. A second reverse material layer is formed over portions of the high selectivity spacer, wherein a top surface of the second reverse material layer is lower than a top surface of the high selectivity spacer. A top portion of the high selectivity spacer is etched back to expose the one or more dummy lines and portions of the hard mask. The dummy lines are removed, and the hard mask is patterned using the high selectivity spacer and the first and second reverse material layers as a mask.

In accordance with an embodiment, a method includes patterning a dummy layer over a mask layer to form one or more dummy lines, forming a spacer layer over top surfaces and sidewalls of the one or more dummy lines, and forming a first reverse material layer over the spacer layer. The spacer layer and the first reverse material layer include different materials. The method further includes patterning the first reverse material layer, removing the one or more dummy lines, and patterning the mask layer using the spacer layer and the first reverse material layer as a mask. Patterning the first reverse material layer includes etching the first reverse material layer at a faster rate than the spacer layer.

In accordance with an embodiment, a method includes forming mandrels over a device layer, forming a spacer layer over a top surface and sidewalls of the mandrels, and forming a first reverse material layer over the spacer layer. The method further includes selectively patterning the first reverse material layer by etching the first reverse material layer at a faster rate than the spacer layer. After patterning, remaining portions of the first reverse material layer are disposed over a first portion of the spacer layer. The method further includes forming a patterned second reverse material layer on a second portion of the spacer layer, and patterning the device layer using the spacer layer, the remaining portions of the first reverse material layer, and the patterned second reverse material layer as a mask.

In accordance with an embodiment, a method includes patterning a dummy layer over a hard mask in a semiconductor device to form one or more dummy lines, depositing a spacer layer over the one or more dummy lines, and forming one or more reverse material layers over the spacer layer. Forming the one or more reverse material layers includes blanket depositing a first one of the one or more reverse material layers, recessing a top surface of the first one of the one or more reverse material layers below a top surface of the spacer layer, and selectively etching the first one of the one or more reverse material layers using a patterned photoresist as a mask. Selectively etching the first one of the one or more reverse material layer includes etching the spacer layer at a lower rate than the first one of the one or more reverse material layers. The method also includes removing lateral portions of the spacer layer to expose the one or more dummy lines, removing the dummy lines, and patterning the hard mask using remaining portions of the spacer layer and the one or more reverse material layers as a mask.

Although the present embodiments and their advantages have been described in detail, it should be understood that various changes, substitutions and alterations can be made herein without departing from the spirit and scope of the disclosure as defined by the appended claims.

Moreover, the scope of the present application is not intended to be limited to the particular embodiments of the process, machine, manufacture, composition of matter, means, methods and steps described in the specification. As one of ordinary skill in the art will readily appreciate from the disclosure, processes, machines, manufacture, compositions of matter, means, methods, or steps, presently existing or later to be developed, that perform substantially the same function or achieve substantially the same result as the corresponding embodiments described herein may be utilized according to the present disclosure. Accordingly, the appended claims are intended to include within their scope such processes, machines, manufacture, compositions of matter, means, methods, or steps. 

What is claimed is:
 1. A method comprising: patterning a dummy layer over a mask layer to form one or more dummy lines; forming a spacer layer over top surfaces and sidewalls of the one or more dummy lines, wherein the spacer layer comprises a metal oxide or a metal nitride, and wherein the forming of the spacer layer comprises forming the spacer layer of titanium nitride or titanium oxide; forming a first reverse material layer over the spacer layer, wherein the spacer layer and the first reverse material layer comprise different materials, and wherein the forming of the first reverse material layer comprises forming the first reverse material layer of spin on glass (SOG); patterning the first reverse material layer, wherein the patterning of the first reverse material layer comprises etching the first reverse material layer at a faster rate than the spacer layer; removing the one or more dummy lines; and patterning the mask layer using the spacer layer and the first reverse material layer as a mask.
 2. The method of claim 1, further comprising: forming a first photoresist over the first reverse material layer; and patterning the first photoresist, wherein patterning the first reverse material layer further comprises etching the first reverse material layer using the first photoresist as a mask.
 3. The method of claim 1, wherein the forming of the spacer layer comprises forming a first portion of the spacer layer over a top surface of the one or more dummy lines to have substantially a same thickness as a second portion of the spacer layer on a sidewall of the one or more dummy lines.
 4. The method of claim 1, wherein the removing of the one or more dummy lines comprises: removing lateral portions of the spacer layer to expose the one or more dummy lines and portions of the mask layer; and using an ashing process to remove the one or more dummy lines.
 5. The method of claim 4, wherein the removing of the lateral portions of the spacer layer comprises using chlorine as an etchant.
 6. The method of claim 1 further comprising prior to the patterning of the first reverse material layer, etching the first reverse material layer so that a top surface of the first reverse material layer is lower than a top surface of the spacer layer.
 7. The method of claim 1, wherein the patterning of the first reverse material layer comprises using tetrafluoromethane, trifluoromethane, difluoromethane, or octafluorocyclobutane as a chemical etchant.
 8. The method of claim 1 further comprising, after the patterning of the first reverse material layer: forming a second photoresist over the spacer layer; forming one or more openings in the second photoresist, exposing the spacer layer; forming a second reverse material layer in the one or more openings; removing the second photoresist; and etching back a top portion of the second reverse material layer to a level below a top surface of the spacer layer.
 9. The method of claim 1, wherein the patterning of the dummy layer comprises patterning the dummy layer at a minimum pitch achievable by a photolithography system.
 10. A method comprising: forming mandrels over a device layer; forming a spacer layer over a top surface and sidewalls of the mandrels; forming a first reverse material layer over the spacer layer; selectively patterning the first reverse material layer by etching the first reverse material layer at a faster rate than the spacer layer, wherein after the selectively patterning of the first reverse material layer, remaining portions of the first reverse material layer are disposed over a first portion of the spacer layer; forming a patterned second reverse material layer on a second portion of the spacer layer; and patterning the device layer using the spacer layer, the remaining portions of the first reverse material layer, and the patterned second reverse material layer as a mask.
 11. The method of claim 10, wherein the spacer layer comprises titanium nitride or titanium oxide, and wherein the first reverse material layer and the patterned second reverse material layer comprise spin on glass.
 12. The method of claim 10 further comprising prior to the selectively patterning of the first reverse material layer, etching back the first reverse material layer to expose a top surface of the spacer layer.
 13. The method of claim 10, wherein the patterning of the device layer comprises using the first reverse material layer to form features of a different width than the remaining portions of the spacer layer.
 14. The method of claim 10, wherein the patterning of the device layer comprises using the patterned second reverse material layer to form features in a perpendicular direction to the remaining portions of the spacer layer.
 15. The method of claim 10, wherein the forming of the patterned second reverse material layer comprises: forming a mask layer over spacer layer; patterning one or more openings in the mask layer to expose the second portion of the spacer layer; depositing a material of the patterned second reverse material layer in the one or more openings; and removing the mask layer.
 16. The method of claim 10 further comprising after the forming of the patterned second reverse material layer, removing the mandrels.
 17. A method comprising: patterning a dummy layer over a hard mask in a semiconductor device to form one or more dummy lines; depositing a spacer layer over the one or more dummy lines; forming one or more reverse material layers over the spacer layer, wherein the forming of the one or more reverse material layers comprises: blanket depositing a first one of the one or more reverse material layers; recessing a top surface of the first one of the one or more reverse material layers below a top surface of the spacer layer; and selectively etching the first one of the one or more reverse material layers using a patterned photoresist as a mask, wherein the selectively etching of the first one of the one or more reverse material layers comprises etching the spacer layer at a lower rate than the first one of the one or more reverse material layers; removing lateral portions of the spacer layer to expose the one or more dummy lines; removing the dummy lines; and patterning the hard mask using remaining portions of the spacer layer and the one or more reverse material layers as a mask.
 18. The method of claim 17 further comprising: after the selectively etching of the first one of the one or more reverse material layers, forming a patterned second one of the one or more reverse material layers adjacent the first one of the one or more reverse material layers.
 19. The method of claim 17, wherein the spacer layer comprises titanium nitride or titanium oxide, and wherein the one or more reverse material layers comprise spin on glass. 